PRODUCT - Flexible circuit conductive carbon paste - CCI-305J (ultra-low resistance type)
Conductive carbon paste CCI-305J
CCI-305J conductive carbon paste Senndai Electronic Materials Co., Ltd. is a fast-drying temperature curing low-impedance conductive carbon paste. It is cured thermoplastic resin refinements made by the ultra-fine toner and low temperature, suitable for screen printing. It can be widely used in membrane switches, flexible printed circuit, for use on PET, PVC sheet, with good printability, conductivity, compatibility, hardness and strong adhesion.
- Features
- Parameters
- Dimensions
First, the main features
1, packing: Toner
2, a solid content (WT%) 30-40
3, a density (g / cm3) 1.0-1.3
4, the viscosity (CPS) 13,000-30,000 (rotational viscometer, Ⅱ units, 75rpm, 25 ℃)
5, the coating area (cm2 / g) (depending on the film thickness) 100-200
6, square resistance (Ω / □ / 25.4цm) ≤10
7, adhesion (3M600 tape, vertical pull) with no loss
8, hardness> H
9, flexibility (wire width 1mm, 2 公斤 × 180 ° outer flap × 1 分钟 × 10 times) △ R <20% R
Second, the use
1, the substrate PET;
2, 200-300 mesh stainless steel screen mesh or polyester screen printing;
3, diluent JX dedicated carbon paste or 783 dilution solvent dilution, should be fully mixed before use;
4, the curing process (recommended) 120 ℃ × 15 min;
5, cleaning agents cyclohexanone;
6, the storage room temperature storage, unopened storage period at six months or more;
7, packaging 1.00 kg (or according to requirements)
Third, the operation and safety
CCI-305J conductive carbon paste containing organic solvents, should be used to maintain ventilation to avoid excessive internal steam inhalation: In case of contact with the skin, should be cleaned with water and soap.
1, packing: Toner
2, a solid content (WT%) 30-40
3, a density (g / cm3) 1.0-1.3
4, the viscosity (CPS) 13,000-30,000 (rotational viscometer, Ⅱ units, 75rpm, 25 ℃)
5, the coating area (cm2 / g) (depending on the film thickness) 100-200
6, square resistance (Ω / □ / 25.4цm) ≤10
7, adhesion (3M600 tape, vertical pull) with no loss
8, hardness> H
9, flexibility (wire width 1mm, 2 公斤 × 180 ° outer flap × 1 分钟 × 10 times) △ R <20% R
Second, the use
1, the substrate PET;
2, 200-300 mesh stainless steel screen mesh or polyester screen printing;
3, diluent JX dedicated carbon paste or 783 dilution solvent dilution, should be fully mixed before use;
4, the curing process (recommended) 120 ℃ × 15 min;
5, cleaning agents cyclohexanone;
6, the storage room temperature storage, unopened storage period at six months or more;
7, packaging 1.00 kg (or according to requirements)
Third, the operation and safety
CCI-305J conductive carbon paste containing organic solvents, should be used to maintain ventilation to avoid excessive internal steam inhalation: In case of contact with the skin, should be cleaned with water and soap.